Saeid Sadeghian; Meysam Mahabadi; H. Saadat Hosseini; B. Sabagh
Abstract
Background and aim: Laser ablation as an alternative method for etching porcelain has been proposed. However,previous studies have reported contrasting results. This study is designed to investigate techniques that could obtain maximum bond strength and also modes of their fracture.Materials and method: ...
Read More
Background and aim: Laser ablation as an alternative method for etching porcelain has been proposed. However,previous studies have reported contrasting results. This study is designed to investigate techniques that could obtain maximum bond strength and also modes of their fracture.Materials and method: Fifty samples of porcelain fused to metal according to surface preparation were divided into five groups: 1.HF acid(9.6%) 2. HF acid+ silane 3. Co2 laser (2w, 30 s) 4. Co2 laser+silane 5.removing the glazed layer with diamond bur (controls). After bonding orthodontic brackets and thermocycling process, the shear bond strength (SBS) measured with Instron. Results analyzed by one way ANOVA and Least Significant Difference (p < 0.001). pattern of debonding was investigated with light microscope and results were analyzed by Kruskall wallis and Mann-whitney (p < 0.001).Results: results showed bond strength of Co2 laser (2 w) was clinically high although it was lower than HF acid samples, with better mode of fracture.Conclusion: HF acid in combination with silane showed the highest shear bond strength value while irradiation of grouped pulse Co2 laser for 30 s in combination with silane could be an alternative for HF acid etching.